We use cookies to ensure that we give you the best experience on our website. If you click 'Accept all cookies' we'll assume that you are happy to receive all cookies and you won't see this message again. If you click 'Reject all non-essential cookies' only necessary cookies providing core functionality such as security, network management, and accessibility will be enabled. Click 'Find out more' for information on how to change your cookie settings.

BACKGROUND: The use of highly cross-linked polyethylene is now commonplace in total hip arthroplasty. Hip simulator studies and short-term in vivo measurements have suggested that the wear rate of highly cross-linked polyethylene is significantly less than that of conventional ultra-high molecular weight polyethylene. However, long-term data to support its use are limited. The aim of this study was to compare the intermediate-term steady-state wear of highly cross-linked polyethylene compared with that of conventional ultra-high molecular weight polyethylene acetabular liners in a prospective, double-blind, randomized controlled trial with use of radiostereometric analysis. METHODS: Fifty-four patients were randomized to receive hip replacements with either conventional ultra-high molecular weight polyethylene acetabular liners (Zimmer) or highly cross-linked polyethylene liners (Longevity; Zimmer). All patients received a cemented, collarless, polished, tapered femoral component (CPT; Zimmer) and an uncemented acetabular component (Trilogy; Zimmer). Clinical outcomes were assessed and the three-dimensional penetration of the head into the socket was determined for a minimum of seven years. Linear regression was used to calculate the steady-state wear rate following the creep-dominated penetration seen during the first year. RESULTS: At a minimum of seven years postoperatively, the mean total femoral head penetration was significantly lower in the highly cross-linked polyethylene group (0.33 mm; 95% confidence interval [CI], ±0.10 mm) than it was in the ultra-high molecular weight polyethylene group (0.55 mm; 95% CI, ±0.10 mm) (p = 0.005). The mean steady-state wear rate of highly cross-linked polyethylene was 0.005 mm/yr (95% CI, ±0.015 mm/yr), compared with 0.037 mm/yr (95% CI, ±0.019 mm/yr) for conventional ultra-high molecular weight polyethylene (p = 0.007). No patient in the highly cross-linked polyethylene group had a wear rate above the osteolysis threshold of 0.1 mm/yr, compared with 9% of patients in the ultra-high molecular weight polyethylene group. CONCLUSIONS: This study demonstrates that highly cross-linked polyethylene has a significantly lower steady-state wear rate compared with that of conventional ultra-high molecular weight polyethylene. Longer-term follow-up is required to determine if this will translate into improved clinical performance and longevity of these implants.

Original publication

DOI

10.2106/JBJS.J.00287

Type

Journal article

Journal

J Bone Joint Surg Am

Publication Date

20/04/2011

Volume

93

Pages

716 - 722

Keywords

Adult, Arthroplasty, Replacement, Hip, Coated Materials, Biocompatible, Double-Blind Method, Equipment Failure Analysis, Female, Hip Prosthesis, Humans, Linear Models, Male, Middle Aged, Osteoarthritis, Hip, Polyethylene, Polyethylenes, Prospective Studies, Prosthesis Design, Prosthesis Failure, Surface Properties, Treatment Outcome